电注入退火条件对铸造单晶硅PERC电池抗LID效应影响的研究
CSTR:
作者:
作者单位:

(1. 南京航空航天大学 材料科学与技术学院 江苏省能量转换与技术重点实验室, 南京 210016;2. 苏州腾晖光伏科技有限公司研发部, 江苏 常熟 215542)

作者简介:

王泽辉(1997-),男,江苏人,博士生,研究方向为功能材料的应用;

通讯作者:

中图分类号:

TM914.4

基金项目:

国家自然科学基金项目(61774084); 江苏省前瞻性联合研究项目(BY2016003-09);江苏省科技成果转化专项资金项目(BA2017032).


Influence of Current Injection Annealing Condition on Anti-LID Effect of Casting Monocrystalline Silicon PERC Solar Cells
Author:
Affiliation:

(1. Jiangsu Key Lab. of Materials and Technol. for Energy Conversion, College of Materials Science & Technol., Nanjing University of Aeronautics & Astronautics, Nanjing 210016, CHN;2. Research and Development Department, Suzhou Talesun Solar Technol. Co. Ltd., Changshu 215542, CHN)

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    铸造单晶硅太阳电池由于性价比高,在晶硅太阳能市场占有越来越重要的地位。文章以B和Ga共掺杂的铸造单晶硅钝化发射和背面(PERC)电池为研究对象,采用现有工业生产的电注入退火方法,分别进行了260和180℃温度下的不同电注入条件退火处理和随后的光致衰减(LID)效应分析。分析表明:经180℃的电注入退火处理,电池效率的变化率为-0.64%,经60kW·h的光照后,电池效率比退火前降低了2.79%。而经过260℃的电注入退火处理后,电池效率提高1.12%,且经60kW·h的光照后,电池效率比退火前仅下降1.96%。这些结果说明,260℃的电注入退火条件更适用于铸造单晶硅电池的抗LID处理。

    Abstract:

    Due to their high performance and low price, cast monocrystalline silicon solar cells are becoming more and more important in the PV market. The casting monocrystalline silicon passivated emitter and rear cells (PERC) co-doped with Band Ga were taking as the research object, and treated by current injection annealing under 260 and 180℃. And the light induced degradation (LID) effect before and after annealing process was anlyzed. The results show that the efficiency of the cells annealled under 180℃ will reduce by 0.64%, while after a light exposure for 60kW·h, the efficiency is decreased by 2.79%. On the other hand, after the current injection annealing at 260℃, the efficiency of the solar cell is increased by 1.12%, and after a light exposure treatment for 60kW·h, it is only decreased by 1.96%. All the results prove that current injection annealing at 260℃ is a better condition for the anti-LID treatment.

    参考文献
    相似文献
    引证文献
引用本文
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2019-05-30
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2019-12-13
  • 出版日期:
文章二维码

漂浮通知

①《半导体光电》新近入编《中文核心期刊要目总览》2023年版(即第10版),这是本刊自1992年以来连续第10次被《中文核心期刊要目总览》收录。
②目前,《半导体光电》已入编四个最新版高质量科技期刊分级目录,它们分别是中国电子学会《电子技术、通信技术领域高质量科技期刊分级目录》(T3)、中国图象图形学学会《图像图形领域高质量科技期刊分级目录》(T3)、中国电工技术学会《电气工程领域高质量科技期刊分级目录》(T3)和中国照明学会《照明领域高质量科技期刊分级目录》(T2)。
③关于用户登录弱密码必须强制调整的说明
④《半导体光电》微信公众号“半导体光电期刊”已开通,欢迎关注